以下为美国陶氏PC 201-10塑胶原料物性表：
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | --- | ASTM D-1238 | 10 | g/10min | |
| 密度 | --- | ASTM D-792 | 1200 | kg/m3 | ||
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.15 | % | ||
| 平衡吸水率 | 23℃,相对湿度50% | ASTM D-570 | 0.32 | % | ||
| 物理性能 | 折射率 | --- | ASTM D-542 | 1.586 | --- | |
| 透光率 | --- | ASTM D-1003 | 89 | % | ||
| 模具收缩率 | --- | ASTM D-955 | 0.005-0.007 | mm/mm | ||
| 比重 | --- | ASTM D-792 | 1.2 | --- | ||
| 雾度 | --- | ASTM D-1003 | 0.7-1.5 | % | ||
| 机械性能 | 拉伸强度 | 屈服点 | --- | ASTM D-638 | 60 | MPa |
| 断裂点 | ASTM D-638 | 71 | MPa | |||
| 伸长率 | 屈服点 | --- | ASTM D-638 | 60 | % | |
| 断裂点 | ASTM D-638 | 150 | % | |||
| 拉伸模量 | --- | ASTM D-638 | 2410 | MPa | ||
| 弯曲强度 | --- | ASTM D-790 | 96 | MPa | ||
| 弯曲模量 | --- | ASTM D-790 | 2410 | MPa | ||
| 缺口冲击强度 | 23℃ | ASTM D-256 | 900 | J/m | ||
| 冲击强度 | 23℃ | ASTM D-256 | 未破裂 | --- | ||
| 落锤冲击强度 | 23℃ | ASTM D-3763 | 87 | J | ||
| 洛氏硬度 | --- | ASTM D-785 | 73 | M标度 | ||
| 电气性能 | 辉光灯丝测试 | 2mm | IEC 695-2-1 | 850 | ℃ | |
| 对比电弧径迹指数 | 2mm | IEC 112 | 250 | v | ||
| 介电强度 | 60HZ | ASTM D-149 | 17 | kv/mm | ||
| 损耗因素 | 60Hz | ASTM D-150 | 0.001 | --- | ||
| 体积电阻率 | 23℃,干 | ASTM D-257 | 2.0×1017 | Ω.cm | ||
| 热 性 能 | 平均燃烧程度 | --- | ASTM D-635 | 25 | mm | |
| 热变形温度 | 退火@0.45MPa(4 mm) | ASTM D-648 | 144 | ℃ | ||
| 热变形温度 | 退火@1.82MPa(4 mm) | ASTM D-648 | 141 | ℃ | ||
| 热变形温度 | 未退火@1.82MPa(4 mm) | ASTM D-648 | 128 | ℃ | ||
| 维卡软化点 | 50 C/hour | ASTM D-1525 | 149 | ℃ | ||
| 线性热收缩率 | -40℃-82℃ | ASTM D-696 | 68×10-6 | mm/mm/℃ | ||
| 球状压良温度 | --- | IEC 598-1 | >125 | ℃ | ||
| 其它性能 | 需氧系数 | --- | ASTM D-2863 | 26 | % | |